X22CrMoV12-1 1.4923 Stainless Steel Forging Rings Turbine Guide Ring Forgings Forging Blanks
Short Introduction:
| Largest OD:5000mm |
| Largest Weight:12000kg |
| Surface Finish:3.2um Ra Or As Required. |
| Forging Reduction Min:3.1 Or As Required |
| Rought machining or Finis Machining |
1.4923 Chemical composition
| C:0.18~0.24% | Si:0.1~0.5% |
| Mn:0.4~0.9% | P≤0.025% |
| S≤0.015% | Ni:0.3%~0.8% |
| Cr:11.0~12.5% | Mo:0.8~1.2% |
| V:0.25~0.35% |
Heat Treatment:
Quenching In Oil And Tempering.
Mechanical Properties:
| Thickness | Proof Strength | Tensile Strength | Elongation After facture A% | Reduction in area Z% | Impact energy | Hardness |
| ≤250 | 700 Mpa | 900-1050Mpa | 11/10/8 | 35/35/30 | 25/20/20 | 265~315 |
| >250 | 700 Mpa | 850-1050Mpa | 11/10/8 | 35/35/30 | 25/20/20 | 265~315 |
Certfiticates List:
| Certificates list of Jiangyin Fangyuan | ||
| ISO9001:2008 | ISO14001:2004 | PED Certificate |
| ABS Certficate | BV Certficate | DNV Certificate |
| RINA Certficate | GL Certficate | LR Certficate |
| CCS Certficate | NK Certficate | KR Certficate |
| API-6A Certficate | API-17D Certficate | CNAS Certficate |
The main manufacturing equipments: